Overcoming the strength

Scientific Reports volume 12, Article number: 15411 (2022) Cite this article

996 Accesses

1 Altmetric

Metrics details

High strength steels are becoming more important than ever before for automotive applications to reduce the weight of automobiles and to ensure the safety of passengers. Since increased strength usually results in degraded formability, however, cold forming of high strength steels into final shapes remains a challenge to both automotive manufacturers and suppliers. Here we report novel alloy and processing design concepts that can impart high strength to cold-formable steels, which deviates from the traditional approach of improving the formability of high strength steels. Such designed steel subjected to a designed processing route shows an excellent combination of formability and strength as well as crashworthiness, which is crucial for the safety of passengers in the automobiles. The alloy and processing design concepts used in the present study are based on the utilization of thermally induced austenite to martensite transformation, which imparts high strength to cold-formable austenite by cryogenic treatment.

Advanced high strength steels (AHSS) play an important role in automobile manufacturing since they can meet increasingly stringent requirements of automobile industries for the safety and lightweighting of vehicles1,2. Although there are several variants of light materials such as Al and Mg alloys that can be used for structural components in automobiles, the characteristics of AHSS such as their high strength and low manufacturing cost make them materials of choice over other materials3,4,5. Among several grades of AHSS, hot press forming (HPF) steels, also called press hardening steels, have received a great deal of attention since they offer superior tensile properties along with good dimensional accuracy due to their unique processing route consisting of high temperature forming within austenite region followed by cooling in a die to form low temperature hard phases such as martensite or bainite6,7,8. However, such a processing route has a poor production efficiency and moreover these HPF steels generally suffer from liquid metal embrittlement (LME) or microcracking due to an interaction between coating and substrate during high temperature forming9,10,11,12,13,14. Therefore, a new type of high strength steels is needed, which can be formed to a final shape at low temperatures and does not suffer from LME or microcracking associated with high temperature forming.

Fulfilling the requirement for a combination of high strength and high formability is a challenging task since conventional approaches that improve formability have adverse effects on strength or vice versa. In this regard, the use of metastable austenite as a major constituent phase would be a viable approach since austenite, being a face-centered cubic (fcc) phase, can provide good formability at room temperature and also can provide high strength when the transformation of austenite to martensite is enforced by cooling below their martensite start (Ms) temperature15,16,17,18,19 after forming. Stabilization of austenite at room temperature has traditionally been achieved by adding a fairly large amount of austenite stabilizing elements such as in the cases of classical transformation-induced plasticity (TRIP) steels20 and high Mn steels15,16,21, which are usually subjected to austenitization followed by water quenching (WQ). Considering that the stability of austenite in hypoeutectoid steels would be increased when annealed in (ferrite + austenite) intercritical region as compared to austenitization treatment, a fairly large amount of austenite can be retained in steels with leaner alloy compositions after intercritical annealing (IA) followed by water quenching, which is the basic alloy design concept for medium Mn TRIP steels22,23,24,25,26,27,28,29,30,31,32,33. These medium Mn TRIP steels usually contain 30–70 vol% austenite depending on the alloy compositions and show good formability; however, their yield strength is much lower than that of HPF steels. The yield strength of medium Mn steels, as mentioned previously, can be significantly increased when austenite to martensite transformation is promoted by cooling to low temperature, i.e., by cryogenic treatment. Here, the critical issue is that while austenite to martensite transformation should occur by cryogenic treatment to achieve high strength, a substantial amount of austenite should also be retained after cryogenic treatment to ensure crashworthiness of the final components.

In the present study, by utilizing cryogenic treatment, an attempt has been made to develop the steels that show good formability in the intercritically annealed (IAed) condition as well as high strength in the cryogenic treated condition through the transformation of retained austenite to martensite. The model alloy containing 10Mn, 2Al, and 0.2C was fabricated and its microstructure and mechanical properties were evaluated after IA of hot rolled sheets with various annealing conditions as well as after immersion in liquid N2.

30 kg ingot of the steel with a nominal composition of Fe–10Mn–2Al–0.2C (analyzed composition of Fe–9.9Mn–2.0Al–0.2C in wt%) was fabricated using vacuum induction melting. After homogenization at 1150 °C for 2 h, it was hot rolled between 1050 and 850 °C followed by water quenching to produce 3 mm thick sheet with a total reduction of 95%. The hot-rolled sheet was intercritically annealed at 715 °C, 725 °C, and 735 °C for 30 min followed by water quenching. In addition, the IAed sheets were subjected to immersion into liquid N2 (cryogenic treatment) for 1 h to see its effect on microstructure and tensile properties. Cryogenic treated sheets were also heat treated at 170 °C for 20 min and air cooled to simulate the paint baking cycle of automotive components34,35,36.

Microstructure of the steel was analyzed by X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). EBSD analyses were conducted at the middle of rolled sheets (perpendicular to transverse direction) using a field emission SEM (FE-SEM, JEOL JSM-7100F). EBSD measurements were performed at an accelerating voltage of 15 kV and a step size of 0.05–0.2 µm. EBSD data were then analysed using OIM analysis software ver.8.0 (EDAX Inc.). High angle boundaries (15°–62°) are highlighted in the inverse pole figure (IPF) and phase maps. XRD scans were performed on a Bruker D8 Advance diffractometer using Cu Kα radiation. The obtained XRD data were used to calculate the volume fraction of each constituent phase following the direct comparison method suggested by De et al.37. EBSD was also used to measure the volume fraction of the blocky austenite so that the volume fraction of the lath austenite can be indirectly calculated by subtracting the volume fraction of the blocky austenite measured by EBSD from the total volume fraction of austenite measured by XRD. TEM thin foils were prepared by twin-jet polishing (Tenupol-5, Struers) in a 95% acetic acid + 5% perchloric acid solution at 40 V. TEM examinations were carried out on a JEOL JEM-2100F field emission electron microscope at an operating voltage of 200 kV. The compositions of the phases were measured by energy dispersive X-ray spectroscopy (EDS) in STEM mode.

Tensile specimens were cut along the rolling direction with a gauge length, width, and thickness of 25 mm, 6 mm, and 2.5 mm, respectively, according to ASTM standard E8/E8M. Tensile test was conducted at an initial strain rate of 10–3 s−1, using an Instron 8801 universal testing machine.

Bending tests were performed following the guidelines of the ISO 743838 of the International Organization for Standardization (ISO) and VDA 238-10039 of the German Association of the Automotive Industry. The rectangular specimens with a length of 60 mm, a width of 30 mm, and a thickness of 1.5 mm were subjected to three-point bending, where the bending axis is parallel with the rolling direction of the sheet, at a punch speed of 20 mm min−1 with a punch radius of 0.4 mm and a roller diameter of 30 mm. Bending angle was measured by the protractor. The R/t ratio was measured as the smallest ratio of the punch radius (R) to the sheet thickness (t) that results in a crack-free bend during bending to an angle of 90°. The punch radii used were 3 mm to 8 mm in 0.5 mm intervals.

Typical microstructure of the steel in as-hot rolled condition is shown in Fig. 1. As shown by EBSD phase map (Fig. 1b), the microstructure consists mostly of body-centered cubic (bcc) phase (marked by green color) with some austenite (marked by red color). It can be seen that most of bcc phase is martensite having the morphology of lath martensite. One interesting feature of the microstructure is that most of austenite in as-hot rolled condition is present in the form of band, which is due to a segregation of Mn frequently observed in medium Mn steels25.

Microstructure of the steel in as-hot rolled condition. (a) EBSD IPF map and (b) EBSD phase map. In (b), austenite and bcc phases are marked by red and green colors, respectively. Scale bar of images corresponds to 10 μm.

Figure 2 shows the microstructure of the specimens subjected to IA at temperatures of 715 °C (referred to as the ‘IA715-WQ’) (Fig. 2a,b), 725 °C (referred to as the ‘IA725-WQ’) (Fig. 2d,e), and 735 °C (referred to as the ‘IA735-WQ’) (Fig. 2g,h) followed by WQ. The microstructure of the IAed specimens resembles the as-hot rolled microstructure such that there is a presence of blocky austenite in band form. Besides the blocky austenite, there is also a presence of austenite having the lath morphology within bcc matrix, which resulted from the precipitation of austenite along lath boundaries of the prior martensite in as-hot rolled specimen26. It can also be seen that there are featureless bcc grains in the vicinity of the blocky austenite (e.g., marked by M in Fig. 2). Measurement of the fraction of austenite in each heat treatment condition by XRD (Table 1) shows that there is only a slight increase in the fraction of austenite when IA temperature increases from 715 °C (61%) to 725 °C (63%), suggesting that the IA temperature giving the largest fraction of austenite would be near 725 °C based on thermodynamic modeling40. A further increase in IA temperature (to 735 °C) results in a rather large decrease in the fraction of austenite (from 63 to 47%). Such variation in the fraction of austenite with IA temperature of the present steel shows the trend same as the one frequently observed in other IAed medium Mn steels24,27,28, due to a change in austenite stability resulting from varying degrees of solute partitioning. The respective fractions of the blocky and lath austenite were calculated following the procedure described in the Methods section and are listed in Table 1, showing that the majority of austenite is present in the lath morphology.

Microstructure of the specimens intercritically annealed (IAed) at different temperatures (a–c). The specimen IAed at 715 °C; EBSD IPF map (a) and EBSD phase map (b) after water quenching (WQ), and EBSD phase map after cryogenic treatment (c). (d–f) The specimen IAed at 725 °C; EBSD IPF map (d) and EBSD phase map (e) after WQ, and EBSD phase map after cryogenic treatment (f). (g–i) The specimen IAed at 735 °C; EBSD IPF map (g) and EBSD phase map (h) after WQ, and EBSD phase map after cryogenic treatment (i). Austenite and bcc phases are marked by red and green colors, respectively. Scale bar of images corresponds to 5 μm.

Representative TEM micrographs of blocky austenite and its surrounding area are shown in Fig. 3. EDS analysis (Fig. 3b) shows that the blocky austenite is enriched with Mn (~ 13.1 wt%), but depleted in Al (~ 0.9 wt%). In the vicinity of the blocky austenite, there exist martensite islands having the Mn content (~ 10.8 wt.%) lower than that in the blocky austenite. Comparison with EBSD maps (Fig. 2a,b) shows that the featureless bcc grains (e.g., marked by M in Fig. 2a,b) surrounding the blocky austenite are indeed martensite. Further away, there is a lamellar structure consisting of ferrite, martensite, and austenite laths, whose details are shown in Fig. 3c. Similar to the blocky austenite, lath austenite is also enriched with Mn, whose Mn content is similar (~ 12.8 wt%) to that of the blocky austenite. Nearby the lath austenite, both ferrite and martensite laths are present, whose identification was made by comparing their dislocation densities (Fig. 3c). Mn content of the lath martensite is ~ 10.4 wt%, which is lower than that of the lath austenite, but higher than that (~ 6.0 wt%) of the nearby lath ferrite. The presence of martensite in the IA715-WQ specimen was not expected since thermodynamic calculation suggests that below the IA temperature forming the largest fraction of retained austenite, there would be no transformation of austenite to martensite upon quenching to room temperature28,40. It is believed that the formation of martensite in the present case is due to an inhomogeneous distribution of Mn in the microstructure, typical of hot-rolled medium Mn steels25. Analyses of the IA725-WQ and IA735-WQ specimens show that their microstructure is basically identical to that of the IA715-WQ specimen, except that Mn content in both blocky and lath austenite decreases with an increase in IA temperature as expected.

TEM micrographs showing the morphologies and compositions of the blocky austenite, lath austenite, and their surrounding areas in the specimen intercritically annealed at 715 °C followed by water quenching. (a) Morphology of the blocky austenite and its surrounding area. (b) Mn and Al concentration profiles of the blocky austenite and its surrounding area. (c) Morphology of the lath austenite and its surrounding area. (d) Mn and Al concentration profiles of the lath austenite and its surrounding area. Scale bars in (a) and (c) correspond to 2 µm and 100 nm, respectively.

After cryogenic treatment, there is a decrease in the amount of austenite for all IA conditions. As shown in Table 1, the largest change in the fraction of austenite upon cryogenic treatment, i.e., transformation ratio, is found in the IA735 specimen, followed by the IA725 and IA715 specimens. To clearly visualize the change in the microstructure upon cryogenic treatment, the areas observed after IA-WQ were also subjected to microstructural analyses after cryogenic treatment, which are shown in Fig. 2c (for the IA715-LN2), Fig. 2f (for the IA725-LN2), and Fig. 2i (for the IA735-LN2). It can be seen that both types of austenite, coarse blocky austenite (for example, marked by white circles) and fine lath austenite (for example, marked by black circles) except in the case of the IA715 specimen (Fig. 2b,c), transform to martensite when subjected to cryogenic treatment. It is noted that not the whole grain of the blocky austenite transforms to martensite upon cryogenic treatment; instead only a portion of austenite grain, particularly located near the periphery of the prior austenite, transforms to martensite. This is mainly because of a concentration gradient in the blocky austenite; there is less amount of Mn near the periphery than the center of the blocky austenite, making the former less stable than the latter. Thus, it can be thought that the blocky austenite retained after cryogenic treatment would be quite stable and beneficial for the mechanical properties of cryogenic treated specimens.

As shown in Table 1, interestingly, quantitative analyses show that the degree of change in the fraction of austenite by cryogenic treatment is different depending on the type of austenite, which is also dependent on the IA temperature. In general, the lath austenite appears to be more thermally stable than the blocky austenite, although their relative stability changes with the IA temperature such that while the lath austenite shows a much lower transformation ratio (i.e., higher thermal stability) than the blocky austenite in the IA715 specimen, they show more or less similar transformation ratios in the IA735 specimen. It is generally known that the stability of austenite depends on several factors: its size41 and morphology42, and solute contents43,44. Although the blocky austenite is more enriched with Mn than the lath austenite, it is thought that the coarse blocky morphology of the blocky austenite is responsible for its lower thermal stability than that of the lath austenite, which is consistent with the result of previous studies showing that the lath austenite is more stable than the blocky austenite22,23,45. Nevertheless, as mentioned previously, the thermal stability of the lath austenite becomes more similar to that of the blocky austenite as the specimens are subjected to higher IA temperatures, indicating that factors other than size and morphology would also play important roles in determining the thermal stability of austenite in the IA725 and IA735 specimens. It is well known that the austenite should have a critical amount of solutes to be retained43,44. Considering that the lath austenite has a steep concentration gradient, only a narrow portion of the lath austenite would be retained upon cryogenic treatment, which becomes more evident in the specimens subjected to higher IA temperature. On the other hand, the blocky austenite has a shallow concentration gradient, so only the areas located near the periphery of the prior austenite would transform to martensite, leaving a rather wide portion of the blocky austenite retained upon cryogenic treatment. These result in the transformation ratio of the lath austenite becoming similar to that of the blocky austenite in the IA725 and IA735 specimens.

Figure 4 shows the engineering stress–strain curves of the steel in as-IAed condition as well as after cryogenic treatment and their tensile properties are summarized in Table 2. In the water quenched (WQed) condition, yield strength (YS) initially decreases when the IA temperature increases from 715 to 725 °C, while ultimate tensile strength (UTS) increases and elongation decreases. Such behavior is consistent with the results of previous studies on IAed medium Mn TRIP steels24,28. With further increasing the IA temperature to 735 °C, there are increases in both YS and UTS, which are mainly due to an increased fraction of martensite with increasing IA temperature. It is noted that all the present specimens subjected to hot rolling followed by IA do not show obvious yield point elongation, which is frequently observed in the cold rolled and IAed medium Mn steels24,28. An absence of discontinuous yielding in the hot rolled and IAed specimens is suggested to be mainly due to the simultaneous straining of ferrite and austenite at an early stage of deformation26. Discontinuous yielding is known to cause substantial surface roughening40,41 and heterogeneous deformation in the coatings that facilitate cracking of the coated layer41, and hence continuous yielding behavior of the present steel is more advantageous for automotive applications than discontinuous yielding behavior found in cold rolled and IAed steels.

Tensile stress–strain curves of the specimens intercritically annealed (IAed) at different temperatures subjected to water quenching (WQ), cryogenic treatment (LN2), and baking treatment. (a) WQed, (b) cryogenic treated, and (c) after baking treatment.

After cryogenic treatment, there are large increases in both YS and UTS as compared to those in the WQed condition. For example, the IA725-LN2 specimen shows YS of 871 MPa (an increase of 477 MPa from the IA725-WQ specimen) and UTS of 1563 MPa (an increase of 194 MPa from the IA725-WQ specimen), with total elongation of ~ 17%. In the case of the IA735-LN2 specimen, its YS and UTS values are 974 MPa and 1654 MPa, respectively, with total elongation of ~ 10%. Such large increases in strength of the cryogenic treated specimens compared to that of the WQed specimens are undoubtedly due to the formation of a large amount of martensite induced by cryogenic treatment. The strength of these specimens is quite comparable to that of 22MnB5 HPF steel, while the elongation of the former is higher than that of the latter6,46, indicating that it is possible to develop the steel having a better combination of tensile properties than that of HPF steel by cryogenic treatment of IAed steel.

Measurement of the fraction of retained austenite in the fractured tensile specimens in cryogenic treated condition by XRD shows that there still exists a substantial amount of austenite (Table 1). As shown in Fig. 5a, while most of the lath austenite transforms to martensite (comparing with Fig. 2f), a rather large amount of the blocky austenite remains untransformed, suggesting that the blocky austenite has a higher mechanical stability than the lath austenite. Such higher mechanical stability of the blocky austenite than that of the lath austenite is mainly due to the former having a much shallower Mn concentration gradient than the latter, as mentioned previously.

EBSD phase map of the broken tensile and bending specimens. (a) tensile specimen intercritically annealed (IAed) at 725 °C followed by cryogenic treatment (tensile direction is horizontal) and (b) bending specimen IAed at 725 °C followed by cryogenic treatment and baking treatment (bending axis is perpendicular to the figure). Austenite and bcc phases are marked by red and green colors, respectively. Scale bars in (a) and (b) correspond to 5 μm and 10 μm, respectively.

As shown above, the present steel shows large elongation values in WQed condition, suggesting its good cold formability. Considering that there is no direct relationship between elongation and formability in AHSS, however, its formability should be evaluated by other methods47. In the present study, bending test was performed on the steel in WQed condition and its R/t ratio, the minimum recommended inside radius of curvature (R) that is necessary to form a 90° bend in a sheet of thickness (t) without failure, was measured to evaluate the steel's formability according to the guidelines of the ISO 743838 and VDA 238-10039, which are the standards in the industry. Bending tests can also be used to evaluate the steel's crashworthiness, as demonstrated by the works of Till et al.48 and Manuel et al.49 showing a clear relationship between full-scale crash test results and the bendability, i.e., bending angle, of AHSS. Hence, the bending test was also conducted on the steel in cryogenic treated condition and its bending angle was measured to evaluate the steel's crashworthiness. It is to be noted that the bending test was conducted with the worst specimen configuration such that the bending axis is in the longitudinal direction, which normally gives worse properties than the one in the transverse direction50,51. Only the IA725 and IA735 specimens were subjected to the bending test since the IA715-LN2 specimen has much lower strength than the HPF steels.

Bending tests of the specimens in WQed conditions show that the IA725-WQ and IA735-WQ specimens have R/t ratios of 2.6 and 5.3, respectively. R/t ratio is typically used for the evaluation of formability of various AHSS34,52 and the lower R/t value indicates the better formability. R/t ratio of the IA725-WQ specimen is lower than those of the cold-formable 1400 MPa grade martensitic steel (R/t = 4) and even the cold-formable 1000 MPa grade dual phase steels (R/t = 3)34,52, indicating its good formability at room temperature. On the other hand, the IA735-WQ specimen would have a difficulty in cold forming.

In the case of the cryogenic treated specimens, bending test as well as additional tensile test were conducted after baking the specimens for 170 °C for 20 min to simulate the heating that occurs in the body paint line35,36,53, whose reason for such heat treatment is explained as follows. Once the steel sheet is stamped to a net shape component, it would be subjected to painting followed by curing, which is known as the paint baking cycle. It is usually conducted at 170 °C for 20 min, which would change the properties of the components. It has been reported that the YS of the HPF steels increases by about 100 MPa by bake hardening34,35,36. Measurement of the bending angles for the cryogenic treated specimens after simulated baking process shows that the IA725-LN2 and IA735-LN2 specimens have bending angles of 82° and 76°, respectively, which are much larger than that (55°) of the 22MnB5 HPF steel52, demonstrating the present steel's excellent crashworthiness. Observation of the fractured IA725-LN2 bending specimen subjected to baking (Fig. 5b) shows that the blocky austenite is still retained without being transformed to martensite, similar to the result of tensile test performed on the IA725-LN2 specimen. Such high mechanical stability of austenite in the baked IA725-LN2 specimen is presumably due to an enhancement of stability of austenite by baking54. It is noted that even the IA735-LN2 specimen shows good crashworthiness after baking treatment, although its room temperature formability, the R/t ratio, is lower than that of the cold-formable martensitic steels having a similar strength level.

As mentioned previously, it has been reported that there is a change in tensile properties of the HPF steels by baking, which might also happen in the present type of steel. Therefore, tensile properties of the IA725-LN2 and IA735-LN2 specimens were evaluated after baking at 170 °C for 20 min. It shows that there is indeed a change in tensile properties as shown in Table 2. After baking, both IA725-LN2 and IA735-LN2 specimens show increases in YS (by 71 MPa and 143 MPa for the IA725-LN2 and IA735-LN2 specimens, respectively) and elongation (by 6.9% and 4.1% for the IA725-LN2 and IA735-LN2 specimens, respectively). Previous studies showed that there is no apparent changes in the fraction of austenite in medium Mn TRIP steels subjected to baking treatments29,30. TEM analysis of the baked IA725-LN2 specimen, however, shows that there is a precipitation of ε-carbide in martensite (Fig. 6), increasing the strength of martensite. In addition, partitioning of C atoms from ferrite and martensite to austenite during baking increases the strength of austenite55. Both of these changes in the microstructure would lead to an increase in YS after baking. In addition, increased mechanical stability of austenite by C partitioning54,55 would lead to an increase in elongation after baking, in contrast to the 22MnB5 HPF steel showing a decrease in elongation after baking36,53.

TEM micrographs showing the precipitation of ε-carbide particles in the specimen intercritically annealed at 725 °C followed by cryogenic treatment and baking treatment. (a) Dark field image of ε-carbide particles. (b) High resolution image of martensite and ε-carbide particles and their corresponding fast Fourier transform patterns. White circle: diffraction spots of martensite in [111] zone axis. Red circle: diffraction spots of the first variant of ε-carbide in [\(2\overline{11 }0\)] zone axis. Yellow circle: diffraction spots of the second variant of ε-carbide in [\(2\overline{11 }0\)] zone axis. Scale bars in (a) and (b) correspond to 20 nm and 2 nm, respectively.

In summary, our alloy and processing design concepts enable the development of the steel having an excellent combination of strength and formability, which are mutually contradicting properties. In addition, the developed steel shows excellent crashworthiness, which is crucial for the safety of passengers in automobiles. Furthermore, the developed steel has a composition that is quite similar to those of other commercial TRIP steels and its processing route does not involve high temperature forming causing harmful interactions between coating and substrates so that the developed steel would be expected to gain acceptance by automotive manufactures.

All data supporting the findings of this study are available from the corresponding author on request.

Bouaziz, O., Zurob, H. & Huang, M. Driving force and logic of development of advanced high strength steels for automotive applications. Steel Res. Int. 84, 937–947 (2013).

CAS Google Scholar

Kuziak, R., Kawalla, R. & Waengler, S. Advanced high strength steels for automotive industry. Arch. Civ. Mech. Eng. 8, 103–117 (2008).

Article Google Scholar

Militzer, M. A synchrotron look at steel. Science 298, 975–976 (2002).

Article CAS PubMed Google Scholar

Ashby, M. F. Materials Selection in Mechanical Design 3rd edn. (Butterworth-Heinemann, 2005).

Google Scholar

Kim, N. J. Critical assessment 6: Magnesium sheet alloys: Viable alternatives to steels?. Mater. Sci. Technol. 30, 1925–1928 (2014).

Article CAS Google Scholar

Karbasian, H. & Tekkaya, A. E. A review on hot stamping. J. Mater. Process. Technol. 210, 2103–2118 (2010).

Article CAS Google Scholar

Chen, J., Li, X. & Han, X. Comprehensive Materials Processing-51.7 Hot Stamping Vol. 5, 351–369 (Elsevier, 2014).

Book Google Scholar

Yun, S. M., Gwon, H., Oh, J. & Kim, S. J. Suppression of coating layer crack by diffusion heat treatment in Al–Si coated HPF steels. Met. Mater. Int. https://doi.org/10.1007/s12540-021-01161-w (2022).

Article Google Scholar

Cho, L., Kang, H., Lee, C. & De Cooman, B. C. Microstructure of liquid metal embrittlement cracks on Zn-coated 22MnB5 press-hardened steel. Scr. Mater. 90, 25–28 (2014).

Article CAS Google Scholar

Lee, C. W., Fan, D. W., Sohn, I. R., Lee, S.-J. & De Cooman, B. C. Liquid-metal-induced embrittlement of Zn-coated hot stamping steel. Metall. Mater. Trans. A 43, 5122–5127 (2012).

Article CAS Google Scholar

Wang, K., Gui, Z., Liu, P., Wang, Y. & Zhang, Y. Cracking behavior of Al-Si coating on hot stamping boron steel sheet. Procedia Eng. 81, 1713–1718 (2014).

Article CAS Google Scholar

Bhattacharya, D. Liquid metal embrittlement during resistance spot welding of Zn-coated high-strength steels. Mater. Sci. Technol. 34, 1809–1829 (2018).

Article CAS Google Scholar

Gui, Z.-X., Liang, W.-K., Liu, Y. & Zhang, Y.-S. Thermo-mechanical behavior of the Al–Si alloy coated hot stamping boron steel. Mater. Des. 60, 26–33 (2014).

Article CAS Google Scholar

Fan, D. W., Kim, H. S., Oh, J.-K., Chin, K.-G. & De Cooman, B. C. Coating degradation in hot press forming. ISIJ Int. 50, 561–568 (2010).

Article CAS Google Scholar

Jeong, K., Jin, J.-E., Jung, Y.-S., Kang, S. & Lee, Y.-K. The effects of Si on the mechanical twinning and strain hardening of Fe–18Mn–0.6 C twinning-induced plasticity steel. Acta Mater. 61, 3399–3410 (2013).

Article ADS CAS Google Scholar

Lee, S., Kim, J., Lee, S.-J. & De Cooman, B. C. Effect of Cu addition on the mechanical behavior of austenitic twinning-induced plasticity steel. Scr. Mater. 65, 1073–1076 (2011).

Article CAS Google Scholar

Kim, J.-K. & De Cooman, B. C. Stacking fault energy and deformation mechanisms in Fe–xMn–06 C–yAl TWIP steel. Mater. Sci. Eng. A 676, 216–231 (2016).

Article CAS Google Scholar

Sun, B. et al. Discontinuous strain-induced martensite transformation related to the Portevin-Le Chatelier effect in a medium manganese steel. Scr. Mater. 133, 9–13 (2017).

Article ADS CAS Google Scholar

Springer, H., Belde, M. & Raabe, D. Combinatorial design of transitory constitution steels: Coupling high strength with inherent formability and weldability through sequenced austenite stability. Mater. Des. 90, 1100–1109 (2016).

Article CAS Google Scholar

Zackay, V. F., Parker, E. R., Fahr, D. & Busch, R. The enhancement of ductility in high-strength steels. ASM Trans. Q. 60, 252–259 (1967).

CAS Google Scholar

Kwon, Y., Zargaran, A., Ryu, J. H. & Kim, N. J. Effect of annealing conditions on the microstructure and tensile properties of 0.5 V containing Fe–16Mn–0.8 C–0.5 Si steel. Scr. Mater. 172, 125–129 (2019).

Article CAS Google Scholar

Xiong, X. C., Chen, B., Huang, M. X., Wang, J. F. & Wang, L. The effect of morphology on the stability of retained austenite in a quenched and partitioned steel. Scr. Mater. 68, 321–324 (2013).

Article CAS Google Scholar

Cai, Z. H., Ding, H., Xue, X. & Xin, Q. B. Microstructural evolution and mechanical properties of hot-rolled 11% manganese TRIP steel. Mater. Sci. Eng. A 560, 388–395 (2013).

Article CAS Google Scholar

Lee, S. & De Cooman, B. C. Annealing temperature dependence of the tensile behavior of 10 pct Mn multi-phase TWIP-TRIP steel. Metall. Mater. Trans. A 45, 6039–6052 (2014).

Article CAS Google Scholar

HajyAkbary, F. et al. A quantitative investigation of the effect of Mn segregation on microstructural properties of quenching and partitioning steels. Scr. Mater. 137, 27–30 (2017).

Article CAS Google Scholar

Han, J., Lee, S.-J., Jung, J.-G. & Lee, Y.-K. The effects of the initial martensite microstructure on the microstructure and tensile properties of intercritically annealed Fe–9Mn–00.5 C steel. Acta Mater. 78, 369–377 (2014).

Article ADS CAS Google Scholar

Li, Z. C., Ding, H., Misra, R. D. K., Cai, Z. H. & Li, H. X. Microstructural evolution and deformation behavior in the Fe-(6, 8.5) Mn-3Al-0.2 C TRIP steels. Mater. Sci. Eng. A 672, 161–169 (2016).

Article CAS Google Scholar

Gibbs, P. J. et al. Austenite stability effects on tensile behavior of manganese-enriched-austenite transformation-induced plasticity steel. Metall. Mater. Trans. A 42, 3691–3702 (2011).

Article CAS Google Scholar

Trang, T. T. T. & Heo, Y. U. The role of austenite stability on the change of fracture mode in a dual-phase medium Mn steel having a lamellar microstructure. Mater. Char. 178, 111264 (2021).

Article CAS Google Scholar

Trang, T. T. T., Jeong, C. G., Lee, D. & Heo, Y. U. Nanosized lamellar structures and tensile properties of intercritical-annealed medium Mn steels containing multiphases. Steel Res. Int. https://doi.org/10.1002/srin.202200233 (2022).

Article Google Scholar

Park, G., Kim, K., Lee, Y., Uhm, S. & Lee, C. Kinetics study on low-temperature tempering of martensitic phase in medium Mn steel weldment during paint-baking heat treatment. Met. Mater. Int. 28, 1157–1168 (2022).

Article CAS Google Scholar

Dehghan, M., Miresmaeili, R., Askari-Paykani, M. & Shahverdi, H. R. Effects of a novel severe plastic deformation approach on microstructural and mechanical characteristics of a medium manganese advanced high strength steel. Met. Mater. Int. 28, 1232–1245 (2022).

Article CAS Google Scholar

Zhang, B. G., Zhang, X. M., Li, H. B. & Liu, H. T. Microstructure characteristics, mechanical properties and strain hardening behavior of nitrogen-bearing Fe-0.2 C-5Mn TRIP steel. Met. Mater. Int. https://doi.org/10.1007/s12540-022-01253-1 (2022).

Article Google Scholar

World Steel Association. Advanced High Strength Steels Application Guidelines, Version 7.0 (World Steel Association, 2021).

Google Scholar

De Castro, M. R., Monteiro, W. A. & Politano, R. Enhancements on strength of body structure due to bake hardening effect on hot stamping steel. Int. J. Adv. Manuf. 100, 771–782 (2019).

Article Google Scholar

Järvinen, H., Honkanen, M., Järvenpää, M. & Peura, P. Effect of paint baking treatment on the properties of press hardened boron steels. J. Mater. Process. Technol. 252, 90–104 (2018).

Article CAS Google Scholar

De, A. K., Murdock, D. C., Mataya, M. C., Speer, J. G. & Matlock, D. K. Quantitative measurement of deformation-induced martensite in 304 stainless steel by X-ray diffraction. Scr. Mater. 50, 1445–1449 (2004).

Article CAS Google Scholar

ISO 7438:2020 Metallic materials-Bend test. International Organization for Standardization (ISO) (2020).

VDA 238-100 Plate bending test for metallic materials. German Association of the Automotive Industry (VDA) (2010).

De Moor, E., Matlock, D. K., Speer, J. G. & Merwin, M. J. Austenite stabilization through manganese enrichment. Scr. Mater. 64, 185–188 (2011).

Article CAS Google Scholar

Jung, Y.-S., Lee, Y.-K., Matlock, D. K. & Mataya, M. C. Effect of grain size on strain-induced martensitic transformation start temperature in an ultrafine grained metastable austenitic steel. Met. Mater. Int. 17, 553–556 (2011).

Article CAS Google Scholar

Bhadeshia, H. K. D. H. & Edmonds, D. V. Bainite in silicon steels: New composition–property approach Part 1. Metal Sci. 17, 411–419 (1983).

Article CAS Google Scholar

Takahashi, M. & Bhadeshia, H. K. D. H. A model for the microstructure of some advanced bainitic steels. Mater. Trans. JIM 32, 689–696 (1991).

Article CAS Google Scholar

Tomita, Y. & Okawa, T. Effect of microstructure on mechanical properties of isothermally bainite-transformed 300M steel. Mater. Sci. Eng. A 172, 145–151 (1993).

Article Google Scholar

Van Dijk, N. H. et al. Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling. Acta Mater. 53, 5439–5447 (2005).

Article ADS CAS Google Scholar

Choi, W. S. & De Cooman, B. C. Characterization of the bendability of press-hardened 22MnB5 steel. Steel Res. Int. 85, 824–835 (2014).

Article CAS Google Scholar

Suppan, C., Hebesberger, T., Pichler, A., Rehrl, J. & Kolednik, O. On the microstructure control of the bendability of advanced high strength steels. Mater. Sci. Eng. A 735, 89–98 (2018).

Article CAS Google Scholar

Till, L. & Markus, P. 1st Int. Conf. Hot Sheet Metal Forming of High-performance Steel. CHS2, 143–151 (2008).

Manuel, M. et al. 3rd Int. Conf. Hot Sheet Metal Forming of High-performance Steel. CHS2, 49–55 (2011).

Arola, A.-M. et al. The effect of mechanical behavior on bendability of ultrahigh-strength steel. Mater. Today Commun. 26, 101943 (2021).

Article CAS Google Scholar

Kaijalainen, A. J., Suikkanen, P., Karjalainen, L. P. & Jonas, J. J. Effect of austenite pancaking on the microstructure, texture, and bendability of an ultrahigh-strength strip steel. Metall. Mater. Trans. A 45, 1273–1283 (2014).

Article CAS Google Scholar

Billur, E. Hot Stamping of Ultra High-Strength Steels From a technological and business perspective (Springer, 2019).

Book Google Scholar

Blesi, B. W., Smith, C., Matlock, D. K. & De Moor, E. Bake hardening behavior of DP, TBF, and PHS steels with ultimate tensile strengths exceeding 1 GPa. Int. J. Adv. Curr. Prac. Mobil. 2(6), 3203–3218 (2020).

Google Scholar

Cai, Z. H., Ding, H., Misra, R. D. K., Kong, H. & Wu, H. Y. Unique impact of ferrite in influencing austenite stability and deformation behavior in a hot-rolled Fe–Mn–Al–C steel. Mater. Sci. Eng. A 595, 86–91 (2014).

Article CAS Google Scholar

Li, S. et al. A novel medium-Mn steel with superior mechanical properties and marginal oxidization after press hardening. Acta Mater. 205, 116567 (2021).

Article CAS Google Scholar

Download references

This work was supported by the POSCO and National Research Council of Science & Technology (NST)—Korea Institute of Materials Science (KIMS) Postdoctoral Fellowship Program for Young Scientists at KIMS in South Korea.

Korea Institute of Materials Science, Changwon, Republic of Korea

Gyeongbae Park

Graduate Institute of Ferrous & Energy Materials Technology, Pohang University of Science and Technology, Pohang, Republic of Korea

A. Zargaran, T. T. T. Trang & N. J. Kim

POSCO Technical Lab., Gwangyang, Republic of Korea

J. K. Oh

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

G.P., J.K.O., and N.J.K. designed experiments; G.P., A.Z., J.K.O., and T.T.T.T. carried out experiments; G.P., A.Z., J.K.O., and N.J.K. interpreted the results; G.P., A.Z., and N.J.K. wrote the paper with feedback from all co-authors.

Correspondence to A. Zargaran or N. J. Kim.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Park, G., Zargaran, A., Oh, J.K. et al. Overcoming the strength–formability trade-off in high strength steels via cryogenic treatment. Sci Rep 12, 15411 (2022). https://doi.org/10.1038/s41598-022-19521-w

Download citation

Received: 30 June 2022

Accepted: 30 August 2022

Published: 14 September 2022

DOI: https://doi.org/10.1038/s41598-022-19521-w

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.