Low temperature superplasticity and thermal stability of a nanostructured low
Scientific Reports volume 5, Article number: 18656 (2016) Cite this article
3773 Accesses
9 Citations
Metrics details
We describe here for the first time the low temperature superplasticity of nanostructured low carbon steel (microalloyed with V, N, Mn, Al, Si and Ni). Low carbon nanograined/ultrafine-grained (NG/UFG) bulk steel was processed using a combination of cold-rolling and annealing of martensite. The complex microstructure of NG/UFG ferrite and 50–80 nm cementite exhibited high thermal stability at 500 °C with low temperature elongation exceeding 100% (at less than 0.5 of the absolute melting point) as compared to the conventional fine-grained (FG) counterpart. The low temperature superplasticity is adequate to form complex components. Moreover, the low strength during hot processing is favorable for decreasing the spring back and minimize die loss.
Superplasticity is characterized as the ability of the material to sustain large plastic strain prior to failure1,2,3, which is well documented for titanium alloys4,5,6. Among the various strengthening mechanisms in metals, grain refinement is considered as the appropriate and convenient method to simultaneously improve both strength and toughness7,8,9,10,11. Nanostructured stainless steels processed via a combination of severe cold deformation (>65%) followed by phase reversion annealing exhibited superior strength-ductility combination including high strength/weight ratio, wear resistance and also favorable cellular activity. In this approach, severe deformation of metastable austenite at room temperature leads to strain-induced transformation of austenite to martensite. On annealing, this severely deformed strain-induced martensite reverts back to austenite either via a martensitic shear or diffusional reversion mechanism12,13,14. Thus, there exists a strong potential for using nanostructured stainless steels in lieu of the conventional coarse-grained counterpart. However, in majority of the nanostructured alloy systems, ductility is limited because of lack of strain hardening ability3,4,5,6,7,8,9,10,11,12,13,14,15,16. Thus, improvement in plasticity continues to be the subject of interest. Attention has also been given to high temperature superplasticity to form complex shaped components and curved parts through grain boundary engineering2,17. In ultrafine-grained (UFG) materials, grain boundary sliding is considered as the most important mechanism of superplasticity. Fine grain size is preferred because the number of grain boundaries involved in sliding is high and the distance for accommodation by diffusion and/or slip is small18. We explore here superplasticity in microalloyed low carbon nanograined/ultrafine-grained (NG/UFG) bulk steel at elevated temperature, but significantly below 0.5 melting point (Tm).
There is no doubt that the application field of superplastic forming will become even more widespread if the deformation temperatures can be lowered because of lower energy consumption and significant reduction in surface oxidation. The superplasticity of nanocrystalline nickel was observed at 470 °C, which corresponds to 0.36 Tm1. Fine-grained AZ91 magnesium alloy exhibited superplastic behavior in the low temperature range of 150–250 °C (0.46–0.57 Tm)19. High carbon fine-grained (FG) steels (containing 1–2% C in weight %) were observed to exhibit superplasticity at 0.5–0.65 Tm and strain rate of ~10−4–10−3 s20,21. It is however, important that the forming steel must possess high thermal stability to retain the fine microstructure and provide outstanding mechanical properties in the final product21. Studies on superplasticity in steels at temperatures less than 0.5 Tm, especially in commonly used low carbon steels, have not been explored to the best of our understanding.
Scanning electron microscopy (SEM) micrographs of the experimental steels subjected to reheating at 900 °C followed by water quenching are presented in Fig. 1a. During reheating of the water-quenched martensitic microstructure, fine austenite nucleated at prior austenite grain boundaries and martensite lath. After the second quenching step, the microstructure consisted of fine martensite plates with the width of ~300–500 nm. The prior austenite grain size was 3–6 μm and 20–30 nm VN precipitates were formed during holding at 900 °C, which were distributed within the prior austenite grains and martensite plates (Fig. 1b). The addition of N to V-microalloyed steels decreased the incubation period for the precipitation of V carbonitride and increased the volume fraction because of higher solubility product of V and N. According to the solubility product of V-N in austenite (equation 1)22, the complete dissolution temperature of VN in the experimental steel is 1102 °C. The pinning effect of VN decreased coarsening rate of prior austenite grains. After cold-rolling to 1.6 mm, the non-uniform martensite plates were obtained with width of 100–150 nm and 150–250 nm (Fig. 1c), while in the 0.9 mm thick cold-rolled plate, the martensite plates with width of 100–150 nm parallel to the rolling direction were obtained (Fig. 1d). Thus, superplasticity was studied in 0.9 mm thick cold-rolled plate because of fine and homogeneous original microstructure.
SEM micrographs of experimental steels subjected to water-quenching and cold-rolling.
(a) reheating at 900 °C, followed by water quenching (b) water quenching steel with high magnification presenting V carbonitride at prior austenite grain boundaries (c) cold rolling of the water quenched steel with 1.6 mm thickness and (d) cold rolling of the water quenched steel with 0.9 mm thickness. The prior austenite grain size was 3–6 μm and the width of martensite plates was refined to 100–150 nm on cold-rolling to 0.9 mm thickness.
When cold-rolled plate of 0.9 mm thickness was annealed at 550 °C for 5 min, recrystallization occurred and the microstructure consisted of UFG (100–300 nm) and few NG (<100 nm) ferrite grains and 50–80 nm precipitates distributed along the grain boundaries. This microstructure is referred as NG/UFG steel (Fig. 2a). On annealing at 650 °C for 5 min, the majority of ferrite was coarsened to 1–3 μm and few ferrite grains of submicron size were observed (Fig. 2b). This FG steel was used as a reference steel to study NG/UFG steel.
SEM micrographs of cold-rolled experimental steel subjected to annealing to obtain NG/UFG and FG microstructure.
(a) 550 °C for 5 min and (b) 650 °C for 5 min. The NG/UFG steel was obtained on annealing at 550 °C and was characterized by a combination of NG/UFG ferrite and 50–80 nm fine precipitates, while FG steel with polygonal ferrite grains of 1–3 μm were obtained on annealing at 650 °C.
The effect of isothermal holding time at 500 °C on thermal stability of NG/UFG steel was studied because this is the temperature at which tensile tests was carried out after annealing. For duration of 5 to 30 min, the NG/UFG ferrite was stable and morphology of few grains was altered from elongated-shape to equiaxed demonstrating further recrystallization (Fig. 3a–c). Two types of precipitates were nucleated, 50–80 nm cementite distributed along ferrite grain boundaries and 10–20 nm V(C,N) precipitates (Fig. 3d–f). Based on the volume fraction of second phases calculated by Thermocalc, the precipitation temperature of cementite was 663 °C and its volume fraction in equilibrium at 550 °C was 1.4%. Therefore, the cementite was completely dissolved during isothermal holding at 900 °C and was precipitated during annealing. The precipitation temperature of V(C,N) was 1115 °C (consistent with 1102 °C calculated by solubility product of V-N in austenite) and its volume fraction in equilibrium at 550 °C was 0.17% (Fig. 4). It is proposed that the addition of a small amount of V was effective in enhancing the microstructural stability of UFG low carbon steel against thermal exposure because nanometer-sized V carbonitrides suppress grain growth, even if recrystallization were to occur23.
SEM micrographs of NG/UFG steel subjected to isothermal holding to determine thermal stability.
Isothermally held at 500 °C for (a) 5 min, (b) 10 min, (c,d) 30 min, (e) chemical composition of precipitate at point 3 and (f) chemical composition of precipitate at point 4. The NG/UFG steel had higher thermal stability at 500 °C and the morphology of elongated-shaped ferrite was altered to equiaxed ferrite on further recrystallization. Cementite of size 50–80 nm was distributed along the ferrite grain boundaries and 10–20 nm V(C,N) precipitates were present in the ferrite matrix.
Volume fraction of second phases calculated by Thermocalc.
The precipitation temperature of V(C,N) and cementite was 1115 °C and 663 °C, respectively.
NG/UFG steels were subjected to tensile tests at room temperature (20 °C) and moderately high temperature (500 °C) and compared with FG steel. Tensile straining NG/UFG steel at 0.00025 s−1 and 20 °C, the yield stress was 1400 MPa and elongation was low at 12% because of absence of work hardening (black curve a in Fig. 5). While the FG steel indicated significant work hardening behavior, with yield strength, tensile strength and elongation of 681 MPa, 704 MPa and 29%, respectively (red curve b in Fig. 5). When the tensile test temperature was 500 °C, the NG/UFG steel tensile strained at 0.00025 s−1, the yield strength and tensile strength were reduced to 400 MPa and 457 MPa, respectively. An important characteristic was that the stress decreased slowly on reaching the peak stress, which depicts high elongation of 95% (blue curve c in Fig. 5). On decreasing the strain rate to 0.0001 s−1, the yield strength and tensile strength were further decreased to 278 MPa and 327 MPa, respectively and the elongation was increased to 106%. During the softening process, non-uniform plastic stage was extended, where the NG/UFG steel continues to sustain load even at extraordinary strain of more than 1.0 (green curve d in Fig. 5). In contrast, FG steel strained at 0.00025 s−1 and 500 °C, was characterized by yield strength and tensile strength of 324 MPa and 343 MPa, respectively. The stress decreased rapidly implying abrupt necking, which resulted in reduced elongation of 57% (pink curve e in Fig. 5). The Young's modulus decreased with increasing test temperature, consistent with the results obtained at high temperature in high strength structural steel, UFG steel and austenitic stainless steel24,25,26. The elastic modulus was reduced with decreasing strain rate, which was also obtained in superplastic stress-strain plot of low carbon steel and FG INCONEL alloy 718SPF27,28.
Stress-strain plots illustrating the deformation behavior of NG/UFG steel and FG steel.
(a) NG/UFG straining at 0.00025 s−1 and 20 °C with tensile strength of 1400 MPa, elongation of 12% and no work hardening, (b) FG straining at 0.00025 s−1 and 20 °C with yield strength of 681 MPa, tensile strength of 704 MPa and elongation of 29%, (c) NG/UFG straining at 0.00025 s−1 and 500 °C with yield strength of 400 MPa, tensile strength of 457 MPa and elongation of 95%, (d) NG/UFG straining at 0.0001 s−1 and 500 °C with yield strength of 278 MPa, tensile strength of 327 MPa and elongation of 106%, (e) FG straining at 0.00025 s−1 and 500 °C with yield strength of 324 MPa, tensile strength of 343 MPa and elongation of 57%.
The formation of NG/UFG grains is attributed to the original martensite structure and subsequent recrystallization process. Tsuji29,30,31 proposed that lath martensite has a three-level hierarchy in this morphology: (I) Lath - single crystal of martensite including high density of lattice defects, (II) Block - aggregation of laths with the same crystallographic relationship and (III) Packet - aggregation of the blocks having identical habit plane. An austenite grain is sub-divided into several packets and blocks during martensite transformation. Majority of the block boundaries and packet boundaries are high-angle boundaries. Thus, martensite has a fine-grained structure in the as-transformed state. Takaki32 proposed that cold rolling of martensitic steel introduces slip bands into the matrix and this results in the destruction of lath martensitic structure and the formation of lamellar dislocation cell structure around slip bands. The volume fraction of such a damaged martensite increases with increasing deformation. The undamaged lath martensitic structure was rarely observed and dislocation density was one order of magnitude higher in specimens subjected to severe cold reduction greater than 80%, leading to increase in nucleation rate of recrystallized ferrite grains. It was also proposed29,32,33 that the blocks and packets of martensite have angular and rugged shape. Such high density of high-angle boundaries and complicated shape of blocks and packets would produce strong constraint effect during plastic deformation. The constraint causes inhomogeneous deformation (grain sub-division) resulting in ultrafine deformed microstructure with large local misorientation. During the annealing process, the deformation-induced damaged martensitic structure transformed into NG/UFG ferritic grains via recovery process involving escape of interstitial C atoms and annihilation of dislocations (also called in situ recrystallization or continuous recrystallization). At the same time, the cementite formed due to supersaturated solid solution of C atoms in the damaged martensitic structure. The nano-scale cementite and V(C,N) precipitates increased the thermal stability of NG/UFG steel because their pinning effect inhibited grain growth.
NG/UFG steel exhibited unusual deformation behavior compared with the FG steel and tensile ductility was decreased from 29% to 12% at 0.00025 s−1 and 20 °C. Song7 proposed that this decrease in tensile ductility at room temperature for majority of UFG steels, especially single phase steels, was mainly due to dynamic recovery and plastic instability. First, dynamic recovery as a softening mechanism is able to reduce the apparent work hardening rate. During deformation, dislocations are trapped at grain boundaries. The kinetics of dynamic recovery are associated with the spreading of trapped lattice dislocations to grain boundaries especially in UFG steels34,35,36. For UFG steel, the time for dislocations to move to grain boundaries is shorter than the time of tensile test37. This decrease in dislocation density reduces accumulation of dislocations inside the grains and consequently leads to less work hardening when compared with corresponding steels of coarse grain size. Second, the decrease in tensile ductility can be explained in terms of plastic instability, which initiates necking due to localized deformation38,39. Ultra grain-refinement greatly increases the flow stress of steels, especially during the early stages of plastic deformation. Grain refinement also leads to reduced work hardening capacity. As a result, plastic instability (necking) occurs at an early stage during tensile test, which results in limited uniform elongation in UFG steels. Moreover, in NG/UFG steels, necking occurs during deformation of Lüders band after the yield drop and work-hardening disappears40.
The elongation of NG/UFG steel at 0.00025 s−1 and 500 °C was greatly enhanced from 57% to 95% in comparison to FG steel. Zhilyaev41 and Nieh42 proposed that grain boundaries play an active role during high-temperature deformation and the increase of effective diffusion coefficient in NG/UFG materials may approach values several orders of magnitude higher in comparison to their coarse-crystalline counterpart. In NG/UFG steels, the deformation mechanism of grain boundary sliding begins to operate and it is necessary for an accommodation process to accompany grain boundary sliding and govern the kinetics of superplasticity. This accommodation process might be grain-boundary migration, recrystallization, diffusional flow, or dislocation slip. The elongation was further increased to 106% at lower strain rate of 0.0001 s−1 and 500 °C, representative of low temperature superplastic behavior. It is proposed43 that as the strain rate is decreased, the average cavity size and roundness coefficient increases. The average roundness coefficient is indicative of the degree of diffusion associated with cavity growth. A roundness coefficient of one indicates a perfect circular shape, while a smaller value of roundness coefficient relates to cavity elongation. The increase in roundness coefficient with decreasing strain rate suggests that cavity growth by diffusion is becoming increasingly significant.
The stress-strain plot at 0.0001 s−1 and 500 °C appeared serrated flow, which was also observed in superplastic stress-strain plot of ultrahigh-carbon steel21,44, aluminum alloy1 and magnesium alloy19, which is presumably related to dynamic strain aging (DSA) or discontinuous recovery and periodic recrystallization involving stress relaxation and transfer during deformation. DSA is generally attributed to additional resistance to dislocation motion produced by the mobility of solute atoms that can diffuse to dislocations above a certain temperature27,45. The serrations resulted from the recurrent pinning of dislocations, such that the dislocations are stopped by obstacles such as precipitates and diffusing solute atoms46. A key feature of thermally activated dislocation motion is that the dislocation moves in a jerky manner because the dislocations spend majority of their time to interact with the local obstacles, such as forests of dislocations, vacancies and solute atoms47. Moreover, DSA effect increased with decrease in strain rate48.
In summary, we have observed that low-carbon steel with NG/UFG ferrite and 50–80 nm cementite has high thermal stability at 500 °C with elongation exceeding 100% (<0.5 Tm). An important implication of the study is that the low strength during hot processing is favorable for decreasing the spring back and minimize die loss. The low temperature superplasticity is satisfactory to forming complex components with low energy consumption and weaker surface oxidation.
The experimental steel was melted in vacuum induction furnace and cast as 50 kg ingot. The nominal chemical composition of the experimental steel in wt% was 0.1 C, 0.16 Si, 1.55 Mn, 0.02 Al, 0.1 V, 0.018N, 0.5–1 Ni and balance Fe. The 45 mm thick slab was heated to 1200 °C for 3 h. After air-cooling to 920 °C, the slab was rolled via 7 passes to a plate of 5.5 mm on a rolling mill with roll diameter of 450 mm. The finish rolling was controlled at 805 °C and then the experimental steels were accelerated cooled to room temperature. The microstructure consisted of polygonal ferrite, acicular ferrite and granular bainite. The martensite phase was absent because deformation inhibited transformation of martensite.
The low carbon NG/UFG V-N microalloyed steel was processed through a combination of cold-rolling and annealing of martensite. In the first step, the 5.5 mm thick and 50 mm width steel was reheated at 900 °C for 5 min in a chamber electric furnace and it took 6 min to reach the isothermal temperature. Then, the plate was water quenched to room temperature at a cooling rate of 90 °C/s to obtain martensitic microstructure. Next, in the second step, after removing the scale, the steel of 5 mm thickness was again cold rolled to 1.6 mm and 0.9 mm in thickness, respectively, with 68% and 82% total reduction and 0.3–0.5 mm reduction was carried out in each pass depending on the rolling resistance. The tensile samples were annealed at 550 °C and 650 °C, respectively, in a tubular furnace, with heating rate of 10 °C/s. Subsequently the specimens was water-quenched to room temperature to avoid the microstructural coarsen.
The specimens for microstructural studies were polished to mirror finish using standard metallographic procedure involving use of SiC paper of different surface roughness, followed by final polishing using diamond paste of particle size of 2.5 μm. The polished specimens were etched with a 4 volume percent nital solution and observed using a Zeiss Ultra 55 SEM with an accelerated voltage of 15 kV. The 1/4 thickness was observed to represent the bulk. Moreover, the high microstructural homogeneity along thickness was obtained due to large total cold rolling reduction. The chemical composition of the precipitates was determined by energy-dispersive X-ray spectroscopy (EDX) with an accelerating voltage of 15 kv and instant probe size of smaller than 10 nm. The theoretical calculations concerning evolution of various phases with temperature, such as V(C,N) and cementite, were studied using Thermocalc combined with TCFE6 database for thermodynamic calculation in equilibrium.
Tensile tests were carried out using dog-bone shaped samples of 10 mm gage length and 5 mm gage width at room temperature and 500 °C at strain rate of 0.0001 s−1 and 0.00025 s−1, respectively, using Shimadzu AG-X universal testing machine. An extensometer was used for the room temperature tests. For tensile at 500 °C, the specimens were heated to 500 °C for 5 min prior to loading. The tensile data presented is an average of five measurements for each test condition.
How to cite this article: Hu, J. et al. Low temperature superplasticity and thermal stability of a nanostructured low-carbon microalloyed steel. Sci. Rep. 5, 18656; doi: 10.1038/srep18656 (2015).
McFadden, S. X., Mishra, R. S., Valiev, R. Z., Zhilyaev, A. P. & Mukherjee, A. K. Low-temperature superplasticity in nanostructured nickel and metal alloys. Nature 398, 684–686 (1999).
Article CAS ADS Google Scholar
Pan, D., Kuwano, S., Fujita, T. & Chen, M. W. Ultra-large room-temperature compressive plasticity of a nanocrystalline metal. Nano Lett. 7, 2108–2111 (2007).
Article CAS ADS Google Scholar
Zhan, G. D., Garay, J. E. & Mukherjee, A. K. Ultralow-temperature superplasticity in nanoceramic composites. Nano Lett. 5, 2593–2597 (2005).
Article CAS ADS Google Scholar
Girault, E., Blandin, J. J., Varloteaux, A., Suéry, M. & Combres, Y. Low temperature superplasticity of a metastable β-titanium alloy. Scr. Metall. Mater. 29, 503–508 (1993).
Article CAS Google Scholar
Sergueeva, A. V., Stolyarov, V. V., Valiev, R. Z. & Mukherjee, A. K. Enhanced superplasticity in a Ti-6Al-4V alloy processed by severe plastic deformation. Scr. Mater. 43, 819–824 (2000).
Article CAS Google Scholar
Zhu, X. J., Tan, M. J. & Zhou, W. Enhanced superplasticity in commercially pure titanium alloy. Scr. Mater. 52, 651–655 (2005).
Article CAS Google Scholar
Song, R., Ponge, D., Raabe, D., Speer, J. G. & Matlock, D. K. Overview of processing, microstructure and mechanical properties of ultrafine grained bcc steels. Mater. Sci. Eng. A 441, 1–17 (2006).
Article Google Scholar
Calcagnotto, M., Adachi, Y., Ponge, D. & Raabe, D. Deformation and fracture mechanisms in fine-and ultrafine-grained ferrite/martensite dual-phase steels and the effect of aging. Acta Mater. 59, 658–670 (2011).
Article CAS Google Scholar
Calcagnotto, M., Ponge, D. & Raabe, D. Effect of grain refinement to 1μm on strength and toughness of dual-phase steels. Mater. Sci. Eng. A 527, 7832–7840 (2010).
Article Google Scholar
Song, R., Ponge, D. & Raabe, D. Mechanical properties of an ultrafine grained C-Mn steel processed by warm deformation and annealing. Acta Mater. 53, 4881–4892 (2005).
Article CAS Google Scholar
Song, R., Ponge, D., Raabe, D. & Kaspar, R. Microstructure and crystallographic texture of an ultrafine grained C-Mn steel and their evolution during warm deformation and annealing. Acta Mater. 53, 845–858 (2005).
Article CAS Google Scholar
Misra, R. D. K. et al. Favorable modulation of pre-osteoblast response to nanograined/ultrafine grained structures in austenitic stainless steel. Adv. Mater. 21, 1280–1285 (2009).
Article CAS ADS Google Scholar
Misra, R. D. K. et al. Microstructure and deformation behavior of phase-reversion-induced nanograined/ultrafine-grained austenitic stainless steel. Metall. Mater. Trans. A 40A, 2498–2509 (2009).
Article CAS ADS Google Scholar
Misra, R. D. K., Thein-Han, W. W., Mali, S. A., Somani, M. C. & Karjalainen, L. P. Cellular activity of bioactive nanograined/ultrafine-grained materials. Acta Biomater. 6, 2826–2835 (2010).
Article CAS Google Scholar
Song, R., Ponge, D. & Raabe, D. Improvement of the work hardening rate of ultrafine grained steels through second phase particles. Scr. Mater. 52, 1075–1080 (2005).
Article CAS Google Scholar
Yen, H. W. et al. Role of stress-assisted martensite in the design of strong ultrafine-grained duplex steels. Acta Mater. 82, 100–114 (2015).
Article CAS Google Scholar
Zhang, H., Zhang, L., Cheng, X. & Bai, B. Superplastic characteristic of Mn–Si–Cr alloyed ultrahigh carbon steel realized through a novel process. Acta Mater. 58, 6173–6180 (2010).
Article CAS Google Scholar
Furuhara, T. & Maki, T. Grain boundary engineering for superplasticity in steels. J. Mater. Sci. 40, 919–926 (2005).
Article CAS ADS Google Scholar
Mabuchi, M., Ameyama, K., Iwasaki, H. & Higashi, K. Low temperature superplasticity of AZ91 magnesium alloy with non-equilibrium grain boundaries. Acta Mater. 47, 2047–2057 (1999).
Article CAS Google Scholar
Wadsworth, J. & Sherby, O. D. Influence of chromium on superplasticity in ultra-high carbon steels. J. Mater. Sci. 13, 2645–2649 (1978).
Article CAS ADS Google Scholar
Zhang, H., Bai, B. & Raabe, D. Superplastic martensitic Mn-Si-Cr-C steel with 900% elongation. Acta Mater. 59, 5787–5802 (2011).
Article CAS Google Scholar
Xu, K., Thomas, B. G. & O’malley, R. Equilibrium model of precipitation in microalloyed steels. Metall. Mater. Trans. A 42, 524–539 (2011).
Article CAS Google Scholar
Park, K. T., Kim, Y. S. & Shin, D. H. Microstructural stability of ultrafine grained low-carbon steel containing vanadium fabricated by intense plastic straining. Metall. Mater. Trans. A 32A, 2373–2381 (2001).
Article CAS ADS Google Scholar
Kocks, U. F. Law for work-hardening and low-temperature creep. J. Eng. Mater-T. 98, 76–85 (1976).
Article CAS Google Scholar
Walser, B. & Sherby, O. D. Mechanical behavior of superplastic ultrahigh carbon steels at elevated temperature. Metall. Trans. A 10, 1461–1471 (1979).
Article Google Scholar
Chen, J., Young, B. & Uy, B. Behavior of high strength structural steel at elevated temperature. J. Struct. Eng. 132, 1948–1954 (2006).
Article Google Scholar
Raj, R. Development of a processing map for use in warm-forming and hot-forming processes. Metall. Trans. A 12, 1089–1097 (1981).
Article CAS Google Scholar
Smith, G. D. & Flower, H. L. Superplastic forming of alloy 718. Adv. Mater. Proc. 145, 32–34 (1994).
CAS Google Scholar
Tsuji, N., Ueji, R., Minamino, Y. & Saito, Y. A new and simple process to obtain nano-structured bulk low-carbon steel with superior mechanical property. Scr. Mater. 46, 305–310 (2002).
Article CAS Google Scholar
Ueji, R., Tsuji, N., Minamino, Y. & Koizumi, Y. Ultragrain refinement of plain low carbon steel by cold-rolling and annealing of martensite. Acta Mater. 50, 4177–4189 (2002).
Article CAS Google Scholar
Kitahara, H., Ueji, R., Tsuji, N. & Minamino, Y. Crystallographic features of lath martensite in low-carbon steel. Acta Mater. 54, 1279–1288 (2006).
Article CAS Google Scholar
Takaki, S., Iizuka, S., Tomimura, K. & Tokunaga, Y. Influence of cold working on recovery and recrystallization of lath martensite in 0.2%C steel. Mater. Trans. JIM 33, 577–584 (1992).
Article CAS Google Scholar
Ohmori, A., Torizuka, S., Nagai, K., Koseki, N. & Kogo, Y. Effect of deformation temperature and strain rate on evolution of ultrafine grained structure through single-pass large-strain warm deformation in a low carbon steel. Mater. Trans. 45, 2224–2231 (2004).
Article CAS Google Scholar
Valiev, R. Z. et al. Deformation behaviour of ultra-fine-grained copper. Acta Metall. Mater. 42, 2467–2475 (1994).
Article CAS Google Scholar
Lian, J., Baudelet, B. & Nazarov, A. A. Model for the prediction of the mechanical behaviour of nanocrystalline materials. Mater. Sci. Eng. A 172, 23–29 (1993).
Article Google Scholar
Łojkowski, W. On the spreading of grain boundary dislocations and its effect on grain boundary properties. Acta Metall. Mater. 39, 1891–1899 (1991).
Article Google Scholar
Park, K. T., Kim, Y. S., Lee, J. G. & Shin, D. H. Thermal stability and mechanical properties of ultrafine grained low carbon steel. Mater. Sci. Eng. A 293, 165–172 (2000).
Article Google Scholar
Wei, Q., Jia, D., Ramesh, K. T. & Ma, E. Evolution and microstructure of shear bands in nanostructured Fe. Appl. Phys. Lett. 81, 1240–1242 (2002).
Article CAS ADS Google Scholar
Wei, Q. et al. Adiabatic shear banding in ultrafine-grained Fe processed by severe plastic deformation. Acta Mater. 52, 1859–1869 (2004).
Article CAS Google Scholar
Tomota, Y., Narui, A. & Tsuchida, N. Tensile behavior of fine-grained steels. ISIJ Int. 48, 1107–1113 (2008).
Article CAS Google Scholar
Zhilyaev, A. L. & Pshenichnyuk, A. I. Superplasticity and Grain Boundaries in Ultrafine-grained Materials. (Fizmatlit, Moscow, 2008); Cambridge Int. Sci. Publ (Cambridge, 2010).
Nieh, T. G., Wadsworth, J. & Sherby, O. D. Superplasticity in Metals and Ceramics. Cambridge University Press (Cambridge, 1997).
Smith, G. D. & Yates, D. H. Superplastic forming of INCONEL Alloy 718SPF. SAMPE, Covina, CA, USA. 3, 207–218 (1992).
Google Scholar
Taleff, E. M., Nagao, M., Higashi, K. & Sherby, O. D. High-strain-rate superplasticity in ultrahigh-carbon steel containing 10 wt.% Al (UHCS-10Al). Scr. Mater. 34, 1919–1923 (1996).
Article CAS Google Scholar
Nakada, Y. & Keh, A. S. Serrated flow in Ni-C alloys. Acta Metall. 18, (1970) 437–443.
Article CAS Google Scholar
Van den Beukel, A. & Kocks, U. F. The strain dependence of static and dynamic strain-aging. Acta Metall. 30, 1027–1034 (1982).
Article CAS Google Scholar
Cheng, J., Nemat-Nasser, S. & Guo, W. A unified constitutive model for strain-rate and temperature dependent behavior of molybdenum. Mech. Mater. 33, 603–616 (2001).
Article Google Scholar
Shen, Y. F., Wang, P. J., Liu, Y. D., Misra, R. D. K. & Zuo, L. Activated dynamic strain aging of a TRIP590 Steel at 300 °C and low strain rate and relationship to structure. Mater. Sci. Eng. A 645, 333–338 (2015).
Article CAS Google Scholar
Download references
The authors gratefully appreciate the financial support by the National High-tech R&D Program (863 Program) No. 2015AA03A501. R.D.K. Misra acknowledges support from the Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, USA.
The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China
J. Hu, L.-X. Du, G.-S. Sun & H. Xie
Department of Metallurgical, Laboratory for Excellence in Advanced Steel Research, Metallurgical and Materials Engineering Program, Materials and Biomedical Engineering University of Texas at El Paso, 79968-0521, TX, USA
R.D.K. Misra
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
J.H., G.-S.S., H.X. and L.-X.D. conceived and designed the experiments based on the recent work of R.D.K.M. on stainless steels that involved severe cold deformation and annealing to obtain NG/UFG structure. J.H. analyzed the sequence data and wrote the paper. J.H., L.-X.D. and R.D.K.M. proposed the mechanisms. All authors reviewed the manuscript.
The authors declare no competing financial interests.
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
Reprints and Permissions
Hu, J., Du, LX., Sun, GS. et al. Low temperature superplasticity and thermal stability of a nanostructured low-carbon microalloyed steel. Sci Rep 5, 18656 (2016). https://doi.org/10.1038/srep18656
Download citation
Received: 16 June 2015
Accepted: 18 November 2015
Published: 21 December 2015
DOI: https://doi.org/10.1038/srep18656
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Journal of Iron and Steel Research International (2022)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.